Nodulizer FeSiMg6RE2 Cast Iron Alloys

 Cast Iron Alloys Globular Graphite Properties Of Cast Iron Containing FeSiMg For Casting
 
 
    Soundness in microstructures with omogeneous composition, littlesegregation and lower MgO content. Stable and even lasting with highabsorption of Mg. Much smaller and globular graphite and highnodularization efficency when treted.
 
    Nodularization temperature is recommended at 1400~1450when melted from a cupola, or at 1450~1500 when from anelectric furnace. Added at 1.5~1.8% when sulphur in the liquidcast iron is as high as 0.065~0.09%, or 1.4%~1.5% when sulphur is as high asa 0.05~0.065%.
 
 
Applications:
   Tundish-cover spheroidisation process is adopted in trial-manufacture. NodulizerFeSiMg6RE2 of low Mg and FeSiMg8RE3 in normal use are experimentalized in the competitive text. The component of FeSiMg6RE2 is as follows, 6.2%Mg, 2.7% RE, 39.5%Si, 2.50%Ca, 2.3%Ba, 0.09%Bi.
 
 
Specifications:
 

Competitive Advantage:

    Unique composition of special nodularizers is welcomed and it can be made and sipplied at convenience.
 
    Supplied in the form of grains(5-25mm) or following special requirement. Packed plastic braids with inner wetresistant plastic film. Per packed parcel is 25kg n.w.